maybe i repeat cating of mens ring
I’d love a sample of a model cured in your box. I am experiencing similar surface finish problems and would love to see if a more acute cure process would help to solve them. Please shoot me an email firstname.lastname@example.org.
How many hours are you curing each side for? Are you seeing the plastic change colors?
It would be my pleasure to process some samples for you. I reached out in an email, but if anyone else is interested, my contact information is on the product website at www.wickedshell.com/curebox
The level of interest from jewelry designers and dentists was totally unexpected. Very welcome, but unexpected.
About an hour each side on something like a 2 mm ladies ring or halo pendant in a small nail light. The plastic is changing colors slightly around the edges but not everywhere. Should I be leaving it until it changes in a uniform way? To the translucent brownish blue color?
I work in a jewelry shop with my brother, and he gets excited to get to casting and pulls the piece out of the UV light even though I suggest we cook it longer. Will a longer, thorough cook improve the burn out and surface finish? Can I insist the resin be cooked to a certain color before it’s cast?
Hopefully, after my brother sees that we can save time on finishing by getting a complete cure he will stop pulling the pieces out before they’re ready!
if you are interested in fast and accurate casting, you can consider our BlueCast resin.
No postcuring need, no exotic washes, no extra sprues, burnout cycle 1h.
Other words you cast metal after 2 hours you finish print.
You can read and see more here Test of Blue-Cast: compatible and castable resin
proszę o kontakt- wyślij mi swój email
( iwona .email@example.com)
pozdrawiam Dariusz S.
Sounds like it is not fully cured. I usually have to cure parts for 8 hours or more per side.
Yes, it should. If the resin isn’t fully cured it will react with the investment causing defects.
I want to try this magic liquid
many thanks for top-valuable post
I don’t cast by myself.
have a question:
if I buy your resin, so
could I send printed piece of your resin to casting company
and could they use it with normal casting process of lost wax casting?
possible to achieve the same result as yours with classical burnout schedule?
Probably they won’t agree for shortened process of burnout just for 1 hour.
(any change for them is not acceptable hehe ) I respect that- no choice actually
BlueCast withstands all casting processes including steam dewaxing wax & resin mixed cylinder and burnout with ramp from 4 to 12 hours.
Ability to sublimate and burn within one hour is a plus we searched for those who need model quickly without wasting time and money leaving oven heated for many hours.
We will post shortly some useful indications about how to prepare models with sprues in order to send them to casting sevice and get back perfect casting, this because many casting service they use exotic sprues and/or “resin processing” that are some case unuseful or sometimes they decrease surface quality.
Looking at the background around the “L” on the shield it looks like the surface is not very smooth - If it was wax i would expect the surface to be perfectly smooth. Is the roughness deliberate or is it in the casting? I ask because this is what I am seeing sometimes when i am casting with cabl02.
do you cast by yourself?
This is the laser print result (point).
Printing can not be done on a smooth surface.
Some horizontal stripes, I support the shelf did not do a good job, but can be polished.
(Sorry my English is not good enough.)
It was a simple casting machine I made.
Cool Thanks - yes i am aware of the stripes and surface bumps caused by the laser curing the resin.
UV resin curing time, not necessarily.
- led 365nm or led 405nm are not important, as long as the surface is dry, not sticky hands.
- 50w light for one hour, temperature 30 ~ 45 C, remove the removal of the bracket (this time the best time to clear the stent, but not polished)
- 100W light for 2 hours, temperature 60-70 C, remove the waiting for cooling the surface hardening, grinding the remaining support points.
(In fact, also tested 30 minutes of light casting, is also successful, relatively thin pieces.)
Temperature is in accordance with the official warming table.
The focus is to flip (inverted), the surface of the pock is because the resin does not flow out, give him time to clean the resin flow,
30 minutes flip once, a total of four times (in accordance with the thickness of the ring to increase or decrease), some bad out of shape, angle can be tilted.
- led 365nm 或是led 405nm 都沒有要緊，只要表面乾燥，不黏手.
- 50w 光照一小時，溫度30~45 C ，取出拆支架(這時候最好清除支架時間，但是不要打磨)
- 100W 光照2小時，溫度60-70 C，取出等待冷卻表面硬化，打磨剩餘的支架點。