From my results the material is somewhat brittle without any aging. That doesn’t mean that it’s a fragile material though or that it’s bad. It just means that it’s so hard that when it does give in, it does it without much bending before failure. Obviously the geometry determines how well the print performs under stress and impact. I just didn’t expect the Standard from perform this well under load, even when I was pulling down hard on the extinguisher. Pleasantly surprised
If you haven’t seen it, check this older thread where I test Standard vs Tough with impact testing using a hammer and vise. The Standard material just shatters into many pieces because it doesn’t flex much and does not absorb impact like the Tough material does. Video: smash testing the Standard resin vs Tough resin.