Thanks! That does make sense - the vast majority of users run much lower PD. Anecdotally, air blasting like @MattRForerunner suggested can work well for certain types of parts if you really need more powder back faster - I’ve attached a chart below for a test build I ran where blue is manual time with a tool (brush), red is with air blasting. The other benefit is that air blasting should not remove the semi-sintered powder on your part, so you should be getting back only good powder.
@Mario_Martinez - I’m curious what your circumstance is as well. What typical packing densities / refresh rates do you run?